Low Carbon
Dry Drawing Lubricants
PANLUBE S14
For the pre-drawing before annealing
Calcium lubricant
For the pre-drawing before annealing, good lubrication.
Pickled and lime coating or mechanical descaling.
PANULBE S209
For the pre-drawing before annealing
Calcium lubricant
For the pre-drawing before annealing.
It leaves very low residual after the furnace.
Surface preparation:
- Shot blasting or pickling and lime.
PANLUBE S2860T
For the pre-drawing before annealing
Polymer lubricant
For the pre-drawing before annealng. It leaves zero residual after the fournace.
Surface preparation:
Shot blasting or pickling and lime.
PANLUBE S933
For the pre-drawing before annealing
Calcium - sodium lubricant
For the pre-drawing, 1-3 dies before annealing.
Surface preparation:
pickled and lime coating or pickled and phosphate coating.
PANULBE S1470
For the final calibration
borax free - sodium lubricant with medium content of fatty acids - low melting point
For the final calibration after annealing and phosphate coating.
Surface preparation:
- Annealing + phosphate and lime / phosphate and soap coating / polymer coating.
PANLUBE S1531
For the final calibration
low borax sodium lubricant with high fat content
For the final calibration after annealing and phosphate coating or polymer coating.
PANULBE S2800V
For low residual and high performance
calcium-aluminium lubricant
In combination with PANCOVER. These products leave a low residual and promote high performance in cold heading operations.
Acid pickling, phosphate coating, lime or reactive stearate coating.
PANULBE S2920V
For low residual and high performance
calcium-sodium lubricant
In combination with PANCOVER. These products leave a low residual and promote high performance in cold heading operations.
Acid pickling, phosphate coating, lime or reactive stearate coating.
Panlube S1300
For the preparation of reactive lubrication bath
borax free, reactive stearate, water soluble
For the preparation of reactive lubrication bath after annealing, pickling and phosphate coating.
Wet Drawing Lubricants
PANULBE L3102
E.P. additives for final calibration before forming opeartion
lubricating oils with E.P. additives
Different viscosity to cover different applications and materials.
E.P. additives for the final calibration before the forming operation.
Fully compatible with the heading oil.
Surface preparation:
- acid pickling and coating
- in-line shot blasting
PANULBE L3104
E.P. additives for final calibration before forming opeartion
lubricating oils with E.P. additives
Different viscosity to cover different applications and materials.
E.P. additives for the final calibration before the forming operation.
Fully compatible with the heading oil.
Surface preparation:
- acid pickling and coating
- in-line shot blasting
PANULBE L3106
E.P. additives for final calibration before forming opeartion
lubricating oils with E.P. additives
Different viscosity to cover different applications and materials.
E.P. additives for the final calibration before the forming operation.
Fully compatible with the heading oil.
1. acid pickling and coating
2. in-line shot blasting
PANLUBE G4210
For final calibration bright finishing
jelly paste
For the final calibration after annealing, bright finishing.
Surface preparation:
- Phosphate and lime
PANULBE G4218
For final calibration bright finishing
jelly paste
For the final calibration after annealing, bright finishing.
Surface preparation:
- Phosphate and lime.
Phosphate Coatings
PANCOVER F4500A
High coating weight, very adherent crystals
zinc phosphates accelerated with nitrate/nitrite
For general applications for cold heading and high carbon steel wire: high coating weight, very adherent crystals.
Suitable for oil and dry lubrication.
It can be used either for batch or in-line treatments.
Surface preparation:
- acid pickling
- shot blasting
PANCOVER F4501P
High coating weight, very adherent crystals
zinc phosphates accelerated with nitrate/nitrite
For general applications for cold heading and high carbon steel wire: high coating weight, very adherent crystals.
Suitable for oil and dry lubrication.
It can be used either for batch or in-line treatments.
Surface preparation:
- acid pickling
- shot blasting
PANCOVER F4640
High coating weight for reactive soap coating
zinc phosphates accelerated with nitrate/chlorite
It is specific for cold heading wire, prepared by acid pickling: high coating weight suitable for the reactive soap coating.
Surface preparation:
- acid pickling
- shot blasting
PANCOVER F4620UN
For smooth and black finish
zinc phosphates accelerated with nitrate/chlorite
Universal product for application on high and low carbon steel, on acid pickled or shot blaster rod.
Single product easy to use, very stable working conditions.
It produces a smooth and black finish on the drawn wire, it can be used fot batch or in-line operations.
Surface preparation:
- acid pickling
- shot blasting
Non Reactive Pre-Coatings
Panlube S1300
For the preparation of finishing coating
borax free, reactive stearate, water soluble
For the preparation of reactive lubrication bath after annealing, pickling and phosphate coating.
PANCOVER 4700
For long storage
chloride and borax free
Borax free pre-coating product for stainless steel wires, bars,tubes and profiles.
Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to moisture pick-up enabling long storage before final use.
Surface preparation:
1. acid pickling
2. shot blasting
3.molten salts descaling
PANCOVER 4730
For long storage
chloride free
Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to pick up moisture enabling long storage before final use.
This product can be used either for stainless steel or carbon steel, batch or in-line treatment, specially indicated for mattress spring wire.
Surface preparation:
1. acid pickling
2. shot blasting
3.molten salts descaling
PANCOVER 4750
For long storage
low borax pre-coating
Low borax pre-coating product. The coating film has a low tendency to moisture pick-up enabling long storage before final use.
Surface preparation:
1. acid pickling
2. shot blasting
PANCOVER 4760
To avoid the presence of boron in waste water
borax free product, special additives have been included to enhance the adherence to the rod/wire surface.
Designed to avoid the presence of boron in waste water. It can be used either on rod or fine wire.
Surface preparation:
1. acid pickling
2. shot blasting
PANCOVER 4770
For high humidity enviroment
very low hygroscopicity, low borax
Particularly indicated for high humidity enviromment.
Surface preparation:
1. acid pickling
2. shot blasting
PANCOVER 4780
For the in-line treatment of multi-wire coating
borax free pre-coating compound , water soluble
It is used for the in-line treatment of multi-wire coating after in-line phosphate.
Surface preparation:
- Shot blasting
- Acid pickling and phosphate coating