Dry Drawing Lubricants

PANLUBE S10

For low and medium speed drawing

calcium lubricant with low fat content

For low and medium speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S14

For medium and high speed drawing

Calcium lubricant with low fat content

For medium speed drawing.

The rod preparation can be

  1. by mechanicals descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S37

For medium and high speed drawing

Calcium lubricant with low fat content

For medium and high speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S39

For medium and high speed drawing

Calcium lubricant with low fat content

For medium and high speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S25

For high speed drawing

Calcium lubricant with low fat content

For high speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S44

For high speed drawing

Calcium lubricant with low fat content

Heavy coating for high speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S40

For high speed drawing

Calcium lubricant with low fat content

For high speed drawing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S55

For high speed drawing

calcium lubricant low fat content

For high speed drawing, high melting point.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S466

For very high speed drawing

calcium - sodium lubricant

For very high speed starting from belt descaler and pre-coated rod. Suitable for in-line machines. To be used on the first block followed by a sodium lubricant.

The rod preparation can be:

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by:

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S27

No residual in the pickling bath after annealing

Calcium lubricant with low fat content

No residual in the pickling bath after annealing.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

 

PANLUBE S433

For machines with limited cooling

Calcium lubricant with low fat content

Contains E.P. additives. It is suitable for machines with limited cooling.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S1400

For redrawing and clean nail wire

borax free sodium lubricant for high fat content

For the final dies or for redrawing of fine wire, clean nail wire.

Sodium lubricants are generally used after a calcium lubricant to obtain a clean surface. They can be used directly from the first pass on coated rod or for big diameters.

 

PANLUBE S240

For big diameters

Calcium lubricant with low fat content

Suitable for big diameters, clean surface.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

it is suitable for pressure dies.

PANLUBE S933

For big diameters

Calcium - sodium lubricant

To be used for big diameters on 2-5 steps when a low residual is required on the finished wire.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

 

PANLUBE S940

For big diameters

calcium - sodium lubricant

To be used for big diameters on 2-5 steps when a low residual is srequired on the finished wire.

The rod preparation can be

  1. by mechanical descaling
  2. by brushing
  3. by abrasive sanding
  4. by acid picking

The rod preparation can be pre-coated by

  1. lime
  2. water soluble carriers

It is suitable for pressure dies.

PANLUBE S1531

For big diameters

low borax sodium lubricant

Suitable for big diameters for the production of clean wire.

Sodium lubricants are generally used after a calcium lubricant to obtain a clean surface. They can be used directly from the first pass on coated rod or for big diameters.

 

PANLUBE S1000

To reduce the final coating or with lime coated rod

Borax free sodium lubricant with medium fat content

Used after a calcium lubricant to reduce the final coating or from the first pass with lime coated rod.
Surface preparation:

Sodium lubricants are generally used after a calcium lubricant to obtain a clean surface. They can be used directly  from the first pass on coated rod or for big diameters.

PANLUBE S1440

For the production of fine wire at very high speed

low borax sodium lubricant

For the production of fine wire at very high speed, up to 40 m/s.

Sodium lubricants are generally used after a calcium lubricant to obtain a clean surface. They can be used directly from the first pass on coated rod or for big diameters.

 

 

Wet Drawing Lubricants

PANLUBE L3000

For high lubrication and high speed

water soluble oil for the preparation of water based solution for wet drawing

High lubrication and high speed for the drawing as low and medium carbon wire and galvanized wire.
Surface preparation:

  1. Galvanized wire

PANLUBE L3019

For high lubrication and high speed

water soluble oil for the preparation of water based solution for wet drawing

High lubrication and high speed with shiny finishing for the production of staple wire.
Surface preparation:

  1. Galvanized wire

PANLUBE L3028

For high lubrication and high speed

water soluble oil for the preparation of water based solution for wet drawing

High lubrication and high speed for the drawing as low and medium carbon wire and galvanized wire.
Surface preparation:

  1. Galvanized wire

PANLUBE L3010

For clean wire

liquid lubricant soluble in water

Specific for the production of low carbon clean wire.

Surface preparation:

  1. Galvanized wire (D.A.G.)
  2. Phosphated coated

PANLUBE G4210

Stable emulsion for multi-die drawing

paste lubricant

It produces very stable emulsions for multi-die drawing of annealed, galvanized or electroplated wires.

Surface preparation:

  • After first drawing or annealing and phosphate coating

 

Non Reactive Pre-Coating

PANCOVER 4700

For long storage

chloride and borax free

Borax free pre-coating product for stainless steel wires, bars,tubes and profiles.

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4730

For long storage

chloride free

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to pick up moisture enabling long storage before final use.
This product can be used either for stainless steel or carbon steel, batch or in-line treatment, specially indicated for mattress spring wire.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4750

For long storage

low borax pre-coating

Low borax pre-coating product. The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling
2. shot blasting

 

PANCOVER 4760

To avoid the presence of boron in waste water

borax free product, special additives have been included to enhance the adherence to the rod/wire surface.

Designed to avoid the presence of boron in waste water. It can be used either on rod or fine wire.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4770

For high humidity environment

very low hygroscopicity, low borax

Particularly indicated for high humidity enviromment.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4780

For the in-line treatment of multi-wire coating

borax free pre-coating compound , water soluble

It is used for the in-line treatment of multi-wire coating after in-line phosphate.

Surface preparation:

  1. Shot blasting
  2. Acid pickling and phosphate coating