Dry Drawing Lubricants

PANLUBE S212

For multiple die at high speed

calcium-sodium lubricant with low fat content

Partially water soluble.
For better cleaning on the final dies a Sodium lubricant is recommended (Panlube S 1400).

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S466

For multiple die at high speed

calcium-sodium lubricant with low fat content

Partially water soluble.
It can be used for multiple die at high speed. For better cleaning on the final dies a Sodium lubricant is recommended (Panlube S 1400).

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

 

PANLUBE S616

For multiple die at high speed

calcium-sodium lubricant with low fat content

Partially water soluble.

It can be used for multiple die at high speed.
For better cleaning on the final dies a Sodium lubricant is recommended (Panlube S 1400).

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S622

For multiple die at high speed

calcium - sodium lubricant with low fat content

Partially water soluble. It can be used for multiple die at high speed. 
For better cleaning on the final dies a Sodium lubricant is recommended (Panlube S 1400).

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S624

For multiple die at high speed

calcium-sodium lubricant with low fat content

Partially water soluble.
For better cleaning on the final dies a Sodium lubricant is recommended (Panlube S 1400).

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S933

For diameters and bright finishing

Calcium - sodium lubricant with medium fat content

Recommended for big diameters, bright finishing, rust protection.

Surface preparation:

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

 

PANLUBE S940

For diameters and bright finishing

calcium - sodium lubricant with medium fat content

Recommended for big diameters, bright finishing, rust protection.

Surface preparation:

  1. acid pickling and lime or pre-coating (PANCOVER)
  2. mechanical descaling
  3. mechanical descaling and brushing
  4. abrasive belt descaling
  5. in-line shot blasting (deblasting process)

The final cleaning is generally obtained by a degreasing solution in the last die box using a single or double rotating die. (See our rotating die box LPL 43/2).

PANLUBE S1030

For high speed drawing

calcium-sodium lubricant with high fat content

Recommended for high speed drawing, to be used on the first dies, followed by S1400 or S1531.

Surface preparation:

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S1400

Fully water soluble

borax free sodium lubricant

 

Fully water soluble, it can be used for all dies in case of lime coating, or after a calcium-sodium lubricant in case of mechanical descaling.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

 

 

PANLUBE S1440

Fully water soluble

low borax sodium lubricant

 

Fully water soluble, it can be used for all dies in case of lime coating, or after a calcium-sodium lubricant in case of mechanical descaling.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

 

 

PANULBE S1450

Fully water soluble

borax free sodium lubricant with medium fat content

Fully water soluble.

It can be used for  all dies in case of lime coating or after a calcium-sodium lubricant in case of mechanical descaling.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE S1531

Fully water soluble

low borax sodium lubricant with high fat content

Fully water soluble, it can be used for  all dies in case of lime coating or after a calcium-sodium lubricant in case of mechanical descaling.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die.

(See our Rotating Die Box LPL 43/2).

PANLUBE S2000

For the production of clean wire

calcium-sodium lubricant

For the production of clean wire.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

Wet Drawing Lubricants

PANLUBE G4210

For bright finishing and corrosion protection

jelly paste

 

Special paste for one die application on lime coated rod, excellent bright finishing and good protection against corrosion.

1. acid pickling and lime or pre-coating (PANCOVER)
2. mechanical descaling
3. mechanical descaling and brushing
4. abrasive belt descaling
5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die.

(See our Rotating Die Box LPL 43/2).

PANLUBE G4218

For bright finishing and corrosion protection

jelly paste

Special paste for one die application on lime coated rod, excellent bright finishing and good protection against corrosion.

1. acid pickling and lime or pre-coating (PANCOVER)

2. mechanical descaling

3. mechanical descaling and brushing

4. abrasive belt descaling

5. in-line shot blasting (Deblasting process).

The final cleaning is generally obtained by a degreasing solution in the last die box using a sigle or duble rotating die. (See our Rotating Die Box LPL 43/2).

PANLUBE G4260

For heavy operation on one die

light green paste

High lubrication paste to be used for heavy operation, one step.

Surface preparation:

  1. acid pickling and lime or pre-coating (PANCOVER)
  2. mechanical descaling
  3. mechanical descaling and brushing
  4. abrasive belt descaling
  5. in-line shot blasting (Deblasting process)

The final cleaning is generally obtained by a degreasing solution in the last die box using a single or double rotating die.

(See our Rotating Die Box LPL 43/2)

PANLUBE L3005

For fine wire with bright finishing

liquid lubricant soluble in water

For wet drawing of fine wire with bright finishing.

Surface preparation:

  1. acid pickling and lime or pre-coating (PANCOVER)
  2. mechanical descaling
  3. mechanical descaling and brushing
  4. abrasive belt descaling
  5. in-line shot blasting (Deblasting process)

The final cleaning is generally obtained by a degreasing solution in the last die box using a single or double rotating die.

(See our Rotating Die Box LPL 43/2)

PANLUBE L3009

To be added to the final degreasing

liquid lubricants soluble in water

To be added at 5% to the final degreasing solution.

Surface preparation:

  1. acid pickling and lime or pre-coating (PANCOVER)
  2. mechanical descaling
  3. mechanical descaling and brushing
  4. abrasive belt descaling
  5. in-line shot blasting (Deblasting process)

The final cleaning is generally obtained by a degreasing solution in the last die box using a single or double rotating die.

(See our Rotating Die Box LPL 43/2)

PANLUBE L3131

For removal of residuals

solvent based lubricant

For removal of the residual lubricant after wet drawing for staple wire.

Surface preparation:

  1. acid pickling and lime or pre-coating (PANCOVER)
  2. mechanical descaling
  3. mechanical descaling and brushing
  4. abrasive belt descaling
  5. in-line shot blasting (Deblasting process)

The final cleaning is generally obtained by a degreasing solution in the last die box using a single or double rotating die. (See our Rotating Die Box LPL 43/2)

Non Reactive Pre-Coatings

PANCOVER 4700

For long storage

chloride and borax free

Borax free pre-coating product for stainless steel wires, bars,tubes and profiles.

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4730

For long storage

chloride free

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to pick up moisture enabling long storage before final use.
This product can be used either for stainless steel or carbon steel, batch or in-line treatment, specially indicated for mattress spring wire.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4750

For long storage

low borax pre-coating

Low borax pre-coating product. The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling
2. shot blasting

 

PANCOVER 4770

For high humidity environment

very low hygroscopicity, low borax

Particularly indicated for high humidity enviromment.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4760

To avoid the presence of boron in waste water

borax free product, special additives have been included to enhance the adherence to the rod/wire surface.

Designed to avoid the presence of boron in waste water. It can be used either on rod or fine wire.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4780

For the in-line treatment of multi-wire coating

borax free pre-coating compound , water soluble

It is used for the in-line treatment of multi-wire coating after in-line phosphate.

Surface preparation:

  1. Shot blasting
  2. Acid pickling and phosphate coating