Dry Drawing Lubricants

PANLUBE S400

Rod breakdown of bead wire

Calcium lubricant with medium content of fatty acids

 

Rod breakdown of bead wire.

Surface preparation:

  1. pickling, phosphate and pre-coating
  2. belt descaling and pre-coating
  3. mechanical descaling and coating (PANCOVER 4750, 4760, 4780)

PANLUBE S410NS

Rod breakdown of bead wire

calcium - sodium lubricant with high content of fatty acids, E.P. additives

Rod breakdown of bead wire.

Surface preparation:

  1. pickling, phosphate and pre-coating
  2. belt descaling and pre-coating
  3. mechanical descaling and coating (PANCOVER 4750, 4760, 4780)

 

PANLUBE S645

Rod breakdown of bead wire

calcium lubricant with low content of fatty acids

Rod breakdown of bead wire.

Surface preparation:

  1. pickling, phosphate and pre-coating
  2. belt descaling and pre-coating
  3. mechanical descaling and coating (PANCOVER 4750, 4760, 4780)

PANLUBE S1250

For second drawing of bead wire

low borax sodium lubricant

To be used for the 2nd drawing after patenting

Surface preparation:

  1. acid pickling, phosphate coating and borax or PANCOVER coating
  2. in-line shot blasting (deblasting process) and PANCOVER borax free coating
  3. mechanical descaling
  4. coil shot blasting and coating
  5. belt descaling and in-line precoating
  6. brushing and in-line coating +C3

 

PANLUBE S1280

For steel cord wire

low borax sodium lubricant with high content of stearic acid, high melting point

For first and second drawing of steel cord wire.

High speed and performance. Pressure dies recommended.

Surface preparation:

pickling and coating (PANCOVER 4750, 4760, 4780)

 

PANLUBE S1285

For steel cord wire

borax free sodium lubricant with high content of stearic acid, 100% environmentally safe

For first and second drawing of steel cord wire.

High speed and performance. Pressure dies recommended.

Surface preparation:

pickling and coating (PANCOVER 4750, 4760, 4780)

 

 

PANLUBE S1440

For steel cord wire

low borax sodium lubricant with high content of stearic acids, high melting point

For first and second drawing of steel cord wire.

High speed and performance. Pressure dies recommended.

Surface preparation:

pickling and coating (PANCOVER 4750, 4760, 4780)

 

 

Wet Drawing Lubricants

PANLUBE P02

For steel cord wire

Polymer - Lubricant dispersion

Water based concentrated dispersion of lubricant substances, based on micronized synthetic resins and polymers and E.P. additives.

For fine diameters.

PANLUBE L3046

For steel cord wire

semisynthetic emulsifiable oil

Wet drawing of steel cord wire.

Surface preparation:

  1. brass coating

Phosphate Coatings

PANCOVER F4550A

For high speed drawing

zinc calcium phosphates accelerated with nitrate/nitrite

Product suitable for high speed drawing for high carbon steel wires.

Surface preparation:

  1. acid pickling

PANCOVER F4551P

For high speed drawing

zinc calcium phosphates accelerated with nitrate/nitrite

Product suitable for high speed drawing for high carbon steel wires.

Surface preparation:

  1. acid pickling

PANCOVER F4500A

High coating weight, very adherent crystals

zinc phosphates accelerated with nitrate/nitrite

For general applications for cold heading and high carbon steel wire: high coating weight, very adherent crystals.

Suitable for oil and dry lubrication.

It can be used either for batch or in-line treatments.

Surface preparation:

  1. acid pickling
  2. shot blasting

PANCOVER F4501P

High coating weight, very adherent crystals

zinc phosphates accelerated with nitrate/nitrite

For general applications for cold heading and high carbon steel wire: high coating weight, very adherent crystals.

Suitable for oil and dry lubrication.

It can be used either for batch or in-line treatments.

Surface preparation:

  1. acid pickling
  2. shot blasting

PANCOVER F4620UN

For smooth and black finish

zinc phosphates accelerated with nitrate/chlorite

Universal product for application on high and low carbon steel, on acid pickled or shot blaster rod.

Single product easy to use, very stable working conditions.

It produces a smooth and black finish on the drawn wire, it can be used fot batch or in-line operations.

Surface preparation:

  1. acid pickling
  2. shot blasting

Non Reactive Pre-Coatings

PANCOVER 4700

For long storage

chloride and borax free

Borax free pre-coating product for stainless steel wires, bars,tubes and profiles.

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4730

For long storage

chloride free

Special additives have been included to enhance the adherence to the rod/wire surface
The coating film has a low tendency to pick up moisture enabling long storage before final use.
This product can be used either for stainless steel or carbon steel, batch or in-line treatment, specially indicated for mattress spring wire.

Surface preparation:

1. acid pickling

2. shot blasting

3.molten salts descaling

 

PANCOVER 4750

For long storage

low borax pre-coating

Low borax pre-coating product. The coating film has a low tendency to moisture pick-up enabling long storage before final use.

Surface preparation:

1. acid pickling
2. shot blasting

 

PANCOVER 4760

To avoid the presence of boron in waste water

borax free product, special additives have been included to enhance the adherence to the rod/wire surface.

Designed to avoid the presence of boron in waste water. It can be used either on rod or fine wire.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4770

For high humidity environment

very low hygroscopicity, low borax

Particularly indicated for high humidity enviromment.

Surface preparation:

1. acid pickling

2. shot blasting

 

PANCOVER 4780

For the in-line treatment of multi-wire coating

borax free pre-coating compound , water soluble

It is used for the in-line treatment of multi-wire coating after in-line phosphate.

Surface preparation:

  1. Shot blasting
  2. Acid pickling and phosphate coating